Dear All
I want to study an O vacancy in 2*2*3 supercell for TiO2. I use from vc-relax to optimize the lattice constant either with atomic relaxation. But from one week ago, the pressure evolved around  0.00 and dident go to zero .for example
              (kbar)     P=    0.07
              (kbar)     P=   -0.45
              (kbar)     P=   -0.23
              (kbar)     P=   -0.25
              (kbar)     P=   -0.34
              (kbar)     P=   -0.40
              (kbar)     P=   -0.36
              (kbar)     P=   -0.14
              (kbar)     P=   -0.57
              (kbar)     P=   -0.41
              (kbar)     P=   -0.45
              (kbar)     P=   -0.83
              (kbar)     P=   -0.45
              (kbar)     P=   -0.37
              (kbar)     P=   -1.58
              (kbar)     P=   -1.00
              (kbar)     P=   -0.71
              (kbar)     P=   -0.73
              (kbar)     P=   -0.61
              (kbar)     P=   -0.58
              (kbar)     P=   -0.39
              (kbar)     P=   -0.89
              (kbar)     P=   -0.58
              (kbar)     P=   -0.33
              (kbar)     P=   -0.37
              (kbar)     P=    0.59
              (kbar)     P=   -0.42
              (kbar)     P=   -0.61
              (kbar)     P=   -1.22
              (kbar)     P=   -1.68
              (kbar)     P=   -0.23
              (kbar)     P=   -0.20
              (kbar)     P=   -0.17
              (kbar)     P=   -0.39
              (kbar)     P=   -0.29
              (kbar)     P=   -0.76
              (kbar)     P=   -0.30
              (kbar)     P=   -0.24
what can I do for this problem?
Here is input file:



 &control
    calculation = 'vc-relax'
    restart_mode='restart',
    prefix='rutile-71atom'
    tstress = .true.
    tprnfor = .true.
    pseudo_dir = './',
    outdir='/ptmp/javad/scratch/'
	nstep=1000,
	dt=100,
 /
 &system
    ibrav=  6 , celldm(1) =17.36,celldm(3)=0.9663585,  nat= 71, ntyp= 2,
    ecutwfc =35.0,ecutrho=400
 /
 &electrons
    diagonalization=''
    mixing_mode = 'plain'
    mixing_beta = 0.7
    conv_thr =  1.0d-4
/
 &IONS
 /
 &CELL
cell_dynamics = 'damp-w',
press=00.0	
 /
ATOMIC_SPECIES
Ti   43.0   Ti.pz-sp-van.UPF
O    16.0   O.pz-van_ak.UPF
ATOMIC_POSITIONS crystal
Ti 0.00000000 0.00000000 0.00000000
Ti 0.50000000 0.00000000 0.00000000
Ti 0.00000000 0.50000000 0.00000000
Ti 0.50000000 0.50000000 0.00000000
Ti 0.00000000 0.00000000 0.33333333
Ti 0.50000000 0.00000000 0.33333333
Ti 0.00000000 0.50000000 0.33333333
Ti 0.50000000 0.50000000 0.33333333
Ti 0.00000000 0.00000000 0.66666667
Ti 0.50000000 0.00000000 0.66666667
Ti 0.00000000 0.50000000 0.66666667
Ti 0.50000000 0.50000000 0.66666667
Ti 0.25000000 0.25000000 0.16666667
Ti 0.75000000 0.25000000 0.16666667
Ti 0.25000000 0.75000000 0.16666667
Ti 0.75000000 0.75000000 0.16666667
Ti 0.25000000 0.25000000 0.50000000
Ti 0.75000000 0.25000000 0.50000000
Ti 0.25000000 0.75000000 0.50000000
Ti 0.75000000 0.75000000 0.50000000
Ti 0.25000000 0.25000000 0.83333333
Ti 0.75000000 0.25000000 0.83333333
Ti 0.25000000 0.75000000 0.83333333
Ti 0.75000000 0.75000000 0.83333333
O  0.65265000 0.15265000 0.00000000
O  0.15265000 0.65265000 0.00000000
O  0.65265000 0.65265000 0.00000000
O  0.15265000 0.15265000 0.33333333
O  0.65265000 0.15265000 0.33333333
O  0.15265000 0.65265000 0.33333333
O  0.65265000 0.65265000 0.33333333
O  0.15265000 0.15265000 0.66666667
O  0.65265000 0.15265000 0.66666667
O  0.15265000 0.65265000 0.66666667
O  0.65265000 0.65265000 0.66666667
O  0.34735000 0.34735000 0.00000000
O  0.84735000 0.34735000 0.00000000
O  0.34735000 0.84735000 0.00000000
O  0.84735000 0.84735000 0.00000000
O  0.34735000 0.34735000 0.33333333
O  0.84735000 0.34735000 0.33333333
O  0.34735000 0.84735000 0.33333333
O  0.84735000 0.84735000 0.33333333
O  0.34735000 0.34735000 0.66666667
O  0.84735000 0.34735000 0.66666667
O  0.34735000 0.84735000 0.66666667
O  0.84735000 0.84735000 0.66666667
O  0.40265000 0.09735000 0.16666667
O  0.90265000 0.09735000 0.16666667
O  0.40265000 0.59735000 0.16666667
O  0.90265000 0.59735000 0.16666667
O  0.40265000 0.09735000 0.50000000
O  0.90265000 0.09735000 0.50000000
O  0.40265000 0.59735000 0.50000000
O  0.90265000 0.59735000 0.50000000
O  0.40265000 0.09735000 0.83333333
O  0.90265000 0.09735000 0.83333333
O  0.40265000 0.59735000 0.83333333
O  0.90265000 0.59735000 0.83333333
O  0.09735000 0.40265000 0.16666667
O  0.59735000 0.40265000 0.16666667
O  0.09735000 0.90265000 0.16666667
O  0.59735000 0.90265000 0.16666667
O  0.09735000 0.40265000 0.50000000
O  0.59735000 0.40265000 0.50000000
O  0.09735000 0.90265000 0.50000000
O  0.59735000 0.90265000 0.50000000
O  0.09735000 0.40265000 0.83333333
O  0.59735000 0.40265000 0.83333333
O  0.09735000 0.90265000 0.83333333
O  0.59735000 0.90265000 0.83333333
K_POINTS automatic
 3 3 2   1 1 1 
 thanks alot